Closed Top Tanks

Layer-49

Closed Top Tanks

PE ROTOMOULDED TANKS

Ideal for use as water or chemical tanks due to inert nature of PE (Polyethylene) to most chemicals. However due to the basic origin of its resins, it is unsuitable for hydrocarbon based solvents. IBCs are excellent transportation tanks and are blow moulded from PE material.

  • Product Features & Advantages
  • Range of Tanks and Dimensions
  • Cylindrical Closed Top Tanks
  • Cylindrical Open Top Tanks
  • PE Resin Specifications
  • General Chemical Resistance Chart
  • Fittings and Accessories Available

Product Description

 

Both-Tanks_Product-Features-and-Advantages

 

 

 

 

SMALL SIZE TANKS
MODEL CAPACITY DIMENSIONS
Gallons Litres Top Diameter/ Bottom Diameter Overall Height
mm inches mm inches
R10CC 200 1.000 1.220 48 1.290 51
R11CD 250 1.125 1.220 54 1.270 51
R12CC 260 1.200 1.220 48 1.490 59
R15CC 330 1.500 1.220 48 1.790 70
R18CC 400 1.800 1.300 51 1.760 69
MEDIUM SIZE TANKS
MODEL CAPACITY DIMENSIONS
Gallons Litres Top Diameter/ Bottom Diameter Overall Height
mm inches mm inches
R27CC 600 2,700 1,500 59 2,030 80
R40CS-(S) 890 4,005 2,500 98 1,000 39
R40CC 1,000 4,500 1,750 69 2,225 88
R55CS 1,200 5,400 2,010 79 2,210 87
R68CS 1,500 6,705 2,400 94 1,960 77
R68CS-(S) 1,500 6,800 1,600 63 3,917 154
R72CS 1,800 8,100 2,080 82 2,920 115
R90CS 2,000 9,000 2,580 102 2,300 91
LARGE SIZE TANKS
MODEL CAPACITY DIMENSIONS
Gallons Litres Top Diameter/ Bottom Diameter Overall Height
mm inches mm inches
R135CS-(2) 3,000 13,500 3,060 120 2,550 100
R135CS-(3) 3,000 13,500 2,500 98 3,200 126
R150CS 3,300 14,850 2,400 94 3,800 150
R180CS 4,000 18,000 3,060 120 3,300 130
R230CS-(2) 5,000 22,500 3,060 120 3,800 150
R230CS-(3) 5,000 22,500 3,700 146 2,730 107
R270CS 6,000 27,000 3,060 120 4,500 177
R300CS 6,700 30,150 3,000 118 4,780 188
R320CS 7,000 32,000 3,200 126 4,580 180
R360CS 8,000 36,000 3,300 130 5,050 199
R450CS 10,000 45,000 3,300 130 6,300 248

 

Model: Series/Body Type/Opening Type

CD = Non Stackable, Fully Detachable Dome Cover
CC = Non Stackable, Manhole At Centre
CS = Non Stackable, Manhole At Side

 

PE RESIN SPECIFICATIONS

Physical Properties Test Method Values
Resin properties(1)    
Melt Index, g/10 min ISO 1133 4
Density, g/cc ISO 1183 0.935
Melting Point, °C DSC 125
Vicat Softening, °C ISO 306 (Method A/120) 118
Crystallisation Point, °C DSC 105
Deflection Temperature Under Load ISO 75 75
Mechanical Properties(1)   Values (2) Values (3)
Hardness Shore D ISO R868 57
Tensile Yield, MPa ISO R527 17 17
Ultimate Tensile, MPa ISO R527 24.7 21.8
Ultimate Elongation, % ISO R527 800 700
Flexural Modulus, 1% Secant, MPa ISO 178 640
Tear Resistance, MPa DIN 53515 145 140
ESCR 50 oC, 100% Antarox, h
10% Antarox, h
ASTM D-1693 >1000

400
Falling Dart Impact, 23 °C, J/mm
-20 °C, J/mm
ISO 6603/2 17
23
17

(1) Typical values, not to be construed as specifications. Users should confirm results with their own tests.
(2) Compression moulded samples.
(3) Rotomolded plates of 3-3 mm thickness

 

GENERAL CHEMICAL RESISTANCE CHART

Chemical Class Polyethylene Resins
Acids, Inorganic
Weak
Strong
Strong Oxidising

E
E
G
Acids, Inorganic
Weak
Strong

E
E
Alcohols E
Aldehydes E
Amines
Aliphatic
Aromatic

E
E
Bases E
Beverages E
Condiments E
Esters G
Foodstuffs E
Glycols
Polyglycols
Polyglycols ethers

E
E
Hydrocarbons
Aliphatic
Aromatic
Chlorinated

N
N
N
Insecticides G
Ketones G
Oils
Essential Oils
Vegetable Oils

F
E
Pharmaceuticals E
Salts E

 

E – Excellent            G – Good
F – Fair                     N – Not Recommended

This table should be used as a guide only.
Source of Information : Dow Plastics

 